| Sit P.; Lu Y.H.; Chen H.; Zhou Z.F.; Shen Y.G.; Li K.Y. | |
| 2005-06-01 | |
| Source Publication | Acta Metallurgica Sinica (English Letters)
 |
| ISSN | 10067191 |
| Volume | 18Issue:3Pages:300-306 |
| Abstract | Friction and sliding wear behaviour of Ti-B-N coatings against AISI440C steel ball and WC-6wt%Co ball were studied by using pin-on-disk tribometer along with microstructure characterization using optical microscopy (OM), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). It is shown that the wear resistance of film depended on the wear mechanism. In the case of AISI440C steel, adhesive wear were pre-dominant and the wear rate increased sharply to a maximum when N content reach -38at.%. This might be related to the change of film microstructure and phase configuration, so the least adhesive transfer of tribo-film was observed. If WC-6wt%Co ball was used, less deformation wear debris was observed, this was responsible for the rise of wear rate. Despite of different wear modes, friction coefficients in both cases were found to depend mainly on the formation and the amount of h-BN phase. Elemental analysis by energy dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS) revealed that oxygen participated in the wear behavior by reacting with films to form the debris comprised of various types of Ti oxide including TiO, TiO and TiO, which increased wear resistance. |
| Keyword | Dry sliding wear Friction coefficient Oxidation Ti-B-N Wear |
| URL | View the original |
| Language | 英語English |
| Fulltext Access | |
| Document Type | Journal article |
| Collection | University of Macau |
| Affiliation | City University of Hong Kong |
| Recommended Citation GB/T 7714 | Sit P.,Lu Y.H.,Chen H.,et al. Composition effect on dry sliding weak behaviors of Ti-B-N thin films[J]. Acta Metallurgica Sinica (English Letters), 2005, 18(3), 300-306. |
| APA | Sit P.., Lu Y.H.., Chen H.., Zhou Z.F.., Shen Y.G.., & Li K.Y. (2005). Composition effect on dry sliding weak behaviors of Ti-B-N thin films. Acta Metallurgica Sinica (English Letters), 18(3), 300-306. |
| MLA | Sit P.,et al."Composition effect on dry sliding weak behaviors of Ti-B-N thin films".Acta Metallurgica Sinica (English Letters) 18.3(2005):300-306. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment